Wear
Resisting Steel & Iron
|
|
|
 |
|
Main Application
|
--High
manganese steel is particularly useful for severe service that combines
abrasion and heavy impact and etc. |
|
Standard
|
Chemical
Composition (%)
|
Mechanical
Properties
|
|
JIS
|
ASTM
|
AISI
|
C
|
Si
|
Mn
|
S
|
P
|
Cr
|
Ni
|
Mo
|
V
|
Yield
Strength Kg/mm3
|
Tensile
Strength Kg/mm3
|
Elongation
%
|
Brinell
Hardness
|
|
SC
Mn H1
|
A-128
|
---
|
0.90-1.30
|
0.80
max
|
11.0-14.0
|
0.10
max
|
0.05
max
|
---
|
---
|
---
|
---
|
---
|
75
min
|
35
min
|
170-220
|
|
SC
Mn H11
|
---
|
---
|
0.90-1.30
|
0.80
max
|
11.0-14.0
|
0.07
max
|
0.04
max
|
1.50-2.50
|
---
|
---
|
---
|
40
min
|
75
min
|
20
min
|
210-220
|
|
SC
Mn H21
|
---
|
---
|
1.00-1.35
|
0.80
max
|
11.0-14.0
|
0.07
max
|
0.04
max
|
2.00-3.00
|
---
|
---
|
0.40-0.70
|
45
min
|
75
min
|
10
min
|
220-240
|
|
|
 |
|
Main Application
|
--Nihard
and high chromium cast iron are used in ceramile industry, griding ball,
mill liners, and etc. |
|
Standard
|
Chemical
Composition (%)
|
Mechanical
Properties
|
|
JIS
|
ASTM
|
AISI
|
C
|
Si
|
Mn
|
S
|
P
|
Cr
|
Ni
|
Mo
|
V
|
Yield
Strength Kg/mm3
|
Tensile
Strength Kg/mm3
|
Elongation
%
|
Brinell
Hardness
|
|
---
|
---
|
---
|
3.00-3.50
|
0.60-0.80
|
0.80-1.00
|
0.20
max
|
0.12
max
|
1.50-2.50
|
4.00-5.00
|
---
|
Cu
1.0
|
---
|
30
min
|
---
|
500
|
|
---
|
---
|
---
|
2.50-3.00
|
0.80-1.20
|
0.40-0.80
|
0.2
|
0.15
|
25-30
|
---
|
---
|
---
|
---
|
40
min
|
---
|
600
|
|
|